Hydrotreating Catalysts
Manufactured according to Standard TU- 2177-004-44912618-00 Rev. 2
Composition:
Aluminum-nickel-molybdenum or aluminum-cobalt-molybdenum alloy
Catalyst TNK-2003 is used for crude oil hydrotreating.
Specifications
| Wt. % | |||
|---|---|---|---|
| Parameter | Standard | ||
| Grade A | Grade B | Grade C | |
|
12.0-15.0 |
12.0-15.0 |
12.0-15.0 |
| Physical Properties | |||
|---|---|---|---|
| Parameter | Standard | ||
| Grade A | Grade B | Grade C | |
| Bulk density, g/cm³, max | 0.8 | 0.8 | 0.67-0.85 |
| Diameter, mm | 1.5-2.5 | 1.5-2.5 | 1.5-2.5 |
| Strength factor, kg/mm, average, min. | 2.0 | 2.0 | 2.0 |
Steady operation ensures quality of the diesel fuel according to EURO-3, EURO-4 standards.
Manufactured according to Standard TU 2177-007-44912618-00 Rev. 1-4
Composition:
Aluminum-cobalt-molybdenum composite
Catalyst TNK-2004 is designed for straight-run petroleum fractions hydrotreating ranging from gasoline fractions to diesel fractions.
The catalyst has high HDS (hydrodesulphurization) and HDN (hydrodenitrogenation) activity; it is effective for reforming feed preparation.
Provides high degree of sulfides conversion and selective hydrogenation of saturated hydrocarbons during hydrotreating of pyrolysis BTX-fractions.
Specifications
| Physical Properties | |
|---|---|
| Parameter | Standard |
| Bulk density, g/cm³, max | 0.60-0.80 |
| Diameter, mm | 2.0±0.5 |
| Strength factor, kg/mm, average, min. | 2.1 |
Process Conditions
Space velocity, h-1 2-6
Temperature, °C 230-420
Pressure, MPa 3.0
Steady operation ensures quality of the diesel fuel according to EURO-3, EURO-4 standards.
Manufactured according to Standard TU 2177-008-44912618-01 Rev.2
Composition:
Aluminum-nickel-molybdenum composite
Catalyst TNK-2103 is designed for hydrotreaters for medium and heavy petroleum distillates in addition to the base catalyst. Promoters are introduced to improve pre-hydroforming process of the feedstock and prevent coke formation.
Specifications
| Physical Properties | ||
|---|---|---|
| Parameter | Standard | |
| Grade A | Grade B | |
| Shape | Hollow Cylinder | Hollow Cylinder |
| Bulk density, g/cm³ | 0.7-1.0 | 0.7-1.0 |
Particle size, mm |
13.0-15.0 4.0-6.0 13.0-15.0 |
6.0-7.0 1.5-2.0 5.0-8.0 |
| Catalyst edgewise crush strength, MPa, min. | 10 | 2.0 |
Manufactured according to Standard TU 20.59.56-030-449-12618-2019
Composition
Aluminum-cobalt-molybdenum or aluminum-nickel-molybdenum composition
Catalyst GO-70R is designed for processing of sour gasoline (reformer feedstock), kerosene, diesel and oil fractions.
Specifications
| Physical Properties | ||
|---|---|---|
| Parameter | Standard | |
| GO-70R (Co) | GO-70R (Ni) | |
| Bulk density, g/cm³ | 0.67-0.85 | 0.67-0.85 |
Diameter, mm |
1.5-2.5 | 1.5-2.5 |
| Strength factor, kg/mm, average, min. | 2.2 | 2.2 |
Process Conditions
Space velocity, h-1 2-6
Temperature, °C 230-420
Pressure, MPa 3.0
Catalyst steady operation ensures quality of the diesel fuel according to EURO-3, EURO-4 standards.
Manufactured according to Standard TU 2177-024-44912618-2009 Rev. 1, 2
Composition
Aluminum-cobalt-molybdenum composition
Catalyst ACM is designed for petroleum products hydrotreating.
Specifications
| Physical Properties | |
|---|---|
| Parameter | Standard |
| Bulk density, g/cm³, max | 0.64-0.74 |
| Diameter, mm | 4.0-5.5 |
| Strength factor, kg/mm, average, min. | 1.2 |
Process Conditions
Space velocity, h-1 2.5-5.0
Temperature, °C 350-420
Pressure, MPa, min 3.0
Composition
Aluminum-cobalt-molybdenum composite
Catalyst TNK-2000 is designed for hydrotreating of sour gasolines – reforming feedstock, kerosene, diesel and oil fractions.
Specifications
| Physical Properties | |
|---|---|
| Parameter | Standard |
| Bulk density, g/cm³, max | 0.67-0.81 |
| Diameter, mm | 1.5-2.5 |
| Strength factor, kg/mm, average, min. | 2.1 |
Process Conditions
Space velocity, h-1 2-6
Temperature, °C 230-420
Pressure, MPa 3.0
Steady operation ensures quality of the diesel fuel according to EURO-3, EURO-4 standards.